Bambu PLA Silk Dual-Color filament is crafted from two individual silk colors seamlessly blended into a single strand. Retaining its silky texture and high-gloss features, this filament transitions between two colors, creating a natural and smooth gradient. You can easily change the visible color by rotating the color-blending filament to different orientations. Ideal for printing aesthetic parts and decorative objects. Elevate your creations with the smooth and captivating allure of PLA Silk Dual-Color filament.
Â
Crafted from two individual colors seamlessly merged into a single filament strand, this filament promises a mesmerizing silk appearance. Simply rotate the model to see different color effects, revealing enchanting color fusions that spark your creativity.
Â
The gloss finish of the model printed by Silk material can be controlled by printing temperature and speed. To get glossier finish, higher printing temperatures and/or lower speeds are recommended.
Recommended settings: nozzle temperature: 230 - 240 °C, outer wall speed: 30 - 60 mm/s
Â
All printing parameters are embedded in RFID, which can be read through Bambu Lab's AMS (Automatic Material System). Load and print! No more tedious setting steps.
Â
| Recommended | Not Recommended | |
| Build Plate |
Cool Plate SuperTack, Smooth PEI Plate, Textured PEI Plate
|
/ |
| Hotend |
Hotend with Hardened Steel Nozzle 0.4 mm
Hotend with Stainless Steel Nozzle 0.2 mm / 0.4 mm
|
Hotend with Hardened Steel Nozzle 0.6 mm / 0.8 mm
|
| Glue | Liquid Glue / Glue Stick | / |
| Recommended Printing Settings | |
| Drying Settings (Blast Drying Oven) | 55 °C，8 h |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 210 - 230 °C |
| Bed Temperature (with Glue) | 35 - 45 °C |
| Printing Speed | < 250 mm/s |
| Physical Properties | |
| Density | 1.32 g/cm³ |
| Vicat Softening Temperature | 56 °C |
| Heat Deflection Temperature | 53 °C |
| Melting Temperature | 152 °C |
| Melt Index | 20.5 ± 1.2 g/10 min |
| Mechanical Properties | |
| Tensile Strength | 27 ± 4 MPa |
| Breaking Elongation Rate | 3.5 ± 0.6 % |
| Bending Modulus | 2370 ± 150 MPa |
| Bending Strength | 66 ± 4 MPa |
| Impact Strength | 24.5 ± 1.7 kJ/m² |
Â
| Color | Hex Code | Display | |
| Velvet Eclipse (Black-Red) | #000000; #A34342 | ||
| Midnight Blaze (Blue-Red) | #0047BB; #7D1B49 | ||
| Neon City (Blue-Magenta) | #0047BB; #BB22A3 | ||
| Gilded Rose (Pink-Gold) | #FF9425; #FCA2BF | ||
| Blue Hawaii (Blue-Green) | #60A4E8; #4CE4A0 | ||